Epoxy Paste 1210
Ramset Epoxy Paste 1210 is a tough 100% solids, trowellable epoxy repair mortar for use in high build concrete repair applications such as: structural repairs to damaged concrete and masonry, filling holes, wide cracks, chips in concrete, filling gaps between steel and concrete and timber and concrete.
Pack Size
- 4ltr
- 20ltr
Before visiting a Stockist or Service Centre, contact them to ensure product availability.
PART NUMBER:
Epoxy Paste 1210
-+PRODUCT INFORMATION
Click on the column headings to reorder the table.
| ITEM CODE | Pack Size | Colour | Chemical Type | VOC Compliant | Material Type | ADD TO TOOLBOX |
|---|---|---|---|---|---|---|
| EP1210L20 | 20ltr | Grey | Epoxy | Yes | Trowellable Paste | |
| EP1210L4 | 4ltr | Grey | Epoxy | Yes | Trowellable Paste |
STEEL ZINC PLATED
STAINLESS STEEL
GALVANISED STEEL
-+FEATURES & BENEFITS
- Sets rock hard
- Bond is stronger than concrete
- High build consistency
- Suitable for filling voids with thick cross-section – low heat generated during cure
- Trowellable
- High compressive strength
- 100% solid epoxy – solvent free and negligible shrinkage
- Water proof when cured
- Equal Parts Mix Ratio – Easy to use and measure
-+APPLICATIONS & TRADES
| Repair broken and spalled concrete | Concreter, Building Contractor, Concrete Remediation, Civil Contractor, Construction Contractor, Formworker |
|---|
-+SPECIFICATIONS
| Appearance | Part A: White Thixotropic Paste |
|---|---|
| Mixed Colour | Light Grey |
| Solid content by weight | 100% |
| Tensile strength | 10 MPa approx. |
| Compressive strength | 65 MPa approx. |
| Flexural strength | 33 MPa approx. |
| Flexural Modulus | 4.1 x 103 MPa |
| Lap Shear CRS | 20 MPa |
| T-Peel Zn Gal | 5 N/mm |
| Service temperature | -10°C to + 50°C |
| Glass Transition Temp (Tg) | 50°C |
| Working Time | 2 hours @ 25°C |
| Mix ratio | 1:1 (part A:B) by volume |
| Min. Application temp. | 10°C |
| Max. Application temp. | 35°C |
| Density | 1.25 kg/Litre |
| Full cure | 1 day at 25°C |